Şen, FarukPakdil, Murat2019-07-162019-07-1620081302-0900https://trdizin.gov.tr/publication/paper/detail/T0RNeE5EQXc=https://hdl.handle.net/20.500.12483/1167In this study, the effect of stacking sequences on failure behavior of pinned composite plates was investigated. The laminated composite plates were made from epoxy matrix and glass fibers as reinforcement material. To observe the influences of joint geometry and stacking sequence on the failure mechanism, failure analysis were carried out experimentally. The nine different laminated composite plates were tested. The edge distance-to-hole diameter ratio (E/D) of specimens was designed from 1 to 6. Besides, the specimen width-to-hole diameter ratio (W/D) was only considered as 6. Experimental results point out that failure behavior is strictly influenced from both stacking sequences and geometrical parameters of composite specimens.Bu çalışmada, pim bağlantısı yapılmış kompozitlerin tabaka dizilişlerinin hasar davranışına etkisi incelenmiştir. Tabakalı kompozit plakalar epoksi matris ve takviye elemanı olarak cam liflerinden üretilmiştir. Bağlantı geometrisinin ve tabaka dizilişinin hasar oluşumu üzerine etkilerini gözlemlemek için hasar analizi deneysel olarak yapılmıştır. Dokuz farklı tabakalı kompozit plaka test edilmiştir. Deney numunelerinin serbest ucunun delik çapına oranı (E/D), 1’den 6’ya kadar farklı boyutlarda tasarlanmıştır. Bunun yanı sıra, numune genişliğinin delik çapına oranı (W/D), tüm numunelerde 6 olarak hazırlanmıştır. Deney sonuçları, kompozit numunelerin hazırlanmasındaki boyut değişkenleri ve tabaka dizilişlerinin hasar davranışını önemli bir biçimde etkilediğini göstermiştir.trinfo:eu-repo/semantics/openAccessMühendislikOrtak DisiplinlerArticle112147151WOS:000447785200010N/A