Oezyilmaz, A. TuncayColak, NureddinOzyilmaz, GulSanguen, A. Kemal2024-09-182024-09-1820070300-9440https://doi.org/10.1016/j.porgcoat.2007.06.003https://hdl.handle.net/20.500.12483/8355Polyaniline and poly(aniline-co-o-anisidine) films were deposited on brass (Cu40Zn). The synthesis processes of homo and copolymer film were carried out under cyclic voltammetric condition from 0.12 M aniline and 0.06 M aniline +0.06 M o-anisidine containing 0.2 M sodium oxalate solutions. Homo and copolymer films were characterized by scanning electron microscopy (SEM). SEM images clearly show that one of the brass electrodes was covered with a black copolymer film of strongly adherent homogeneous characteristic while the other one with a porous dark green homo polymer one. The corrosion performances of coated and uncoated electrodes in 3.5% NaCl were evaluated with the help of AC impedance spectroscopy, anodic polarization plots and open circuit potential-time curves. The protective effect of homo and copolymer films formed on brass Grew in parallel with extended exposure time. It was only observed with copolymer-coated electrode that changes in the charge transfer resistance C of copolymer-coated electrode were related to strong adsorption of copolymer film on the brass surface which led to the formation of a protective oxide layer due to its catalytic behaviour. (c) 2007 Elsevier B.V. All rights reserved.eninfo:eu-repo/semantics/closedAccessbrasspolyamlinecopolymercoatingsEIScorrosionReview Article601243210.1016/j.porgcoat.2007.06.0032-s2.0-34548009863Q1WOS:000249736100004Q2