An experimental study of glass-epoxy laminated composite pin-joints

Abstract

In this study, an experimental failure analysis of glass-epoxy laminated composite joints was performed. The effects of joint geometry and stacking sequences on the failure response were investigated. Therefore, the nine different laminated composite plates were tested. The width-to-hole diameter ratio (W/D) of specimens was designed from 2 to 5, whereas the edge distance-to-hole diameter ratio (E/D) was only considered as 6. According to experimental study results, bearing strengths and failure modes of single pinned composite plates was strictly influenced from both stacking sequences and geometrical parameters.

Bu çalışmada, cam lifi-epoksi tabakalı kompozit pimli bağlantıların hasar analizi deneysel olarak yapılmıştır. Bağlantı geometrisinin ve tabaka dizilişlerinin hasar oluşumu üzerine etkileri incelenmiştir. Bu nedenle, dokuz farklı şekilde tabakalandırılmış kompozit plakalar test edilmiştir. Deney numunelerinin genişliğinin delik çapına oranı (W/D) 2’den 5’e kadar farklı boyutlarda hazırlanırken, numunenin serbest ucunun delik çapına oranı (E/D) sadece 6 olarak hazırlanmıştır. Deneysel olarak yapılan çalışmalardan elde edilen sonuçlara göre, tek pim bağlantılı kompozit plaklarda, yatak mukavemetleri ve hasar tipleri hem geometrik parametrelerden hem de tabaka dizilişlerinden kesinlikle etkilenmektedir.