Yazar "Cetin, Ali Riza" seçeneğine göre listele

Listeleniyor 1 - 3 / 3
  • Küçük Resim
    Öğe
    The effect of luting cement thicknesses on the push-out bond strength of the fiber posts
    (Taylor & Francis Ltd, 2013) Ozcan, Erhan; Cetin, Ali Riza; Tuncdemir, Ali Riza; Ulker, Mustafa
    Objective. The aim of this study was to evaluate the effect of luting cement thicknesses on the push-out bond strength of the fiber posts. Materials and methods. Sixty human maxillary canine teeth were endodontically treated. Post spaces were prepared and root specimens randomly divided into three groups: Group 1: etch-and-rinse (Variolink II/Exite DSC), Group 2: self-etch (Panavia F2.0/ED primer) and Group 3: self-adhesive (Clearfil SA Cement). Then each group was divided into four sub-groups according to the cement thickness, as follows: Sub-group 1: 0.35 mm, Sub-group 2: 0.25 mm, Sub-group 3: 0.15 mm, and Sub-group 4: 0.05 mm. Three slices of 1 mm thickness were obtained from each root specimen (n = 15). Push-out tests were performed and data was analyzed with two-way ANOVA and Tukey tests. Results. The etch-and-rinse system (Variolink II) had a significantly higher bond strength compared with the other systems (p < 0.05). The thickest cement group (0.35 mm) had a significantly lower bond strength compared with the 0.15 and 0.05 mm groups in the etch-and-rinse and self-adhesive groups (p < 0.05). In the self-etch group, the cement thicknesses did not significantly affect the bond strength (p > 0.05). Conclusions. The etch-and-rinse system offered better bonding to root dentine than the self-adhesive and self-etch systems. The increases in cement thickness significantly reduced the bond strength of fiber posts to root dentine for both the etch-and-rinse and self-adhesive systems.
  • Küçük Resim
    Öğe
    Elution of monomer from different bulk fill dental composite resins
    (Elsevier Sci Ltd, 2015) Cebe, Mehmet Ata; Cebe, Fatma; Cengiz, Mehmet Fatih; Cetin, Ali Riza; Arpag, Osman Fatih; Ozturk, Bora
    Objective. The purpose of this study was to evaluate the elution of Bis-GMA, TEGDMA, HEMA, and Bis-EMA monomers from six bulk fill composite resins over four different time periods, using HPLC. Methods. Six different composite resin materials were used in the present study: Tetric Evo Ceram Bulk Fill (Ivoclar Vivadent, Amherst, NY), X-tra Fill (VOCO, Cuxhaven, Germany), Sonic Fill (Kerr, Orange, CA, USA), Filtek Bulk Fill (3M ESPE Dental Product, St. Paul, MN), SDR (Dentsply, Konstanz, Germany), EQUIA (GC America INC, Alsip, IL). The samples (4 mm thickness, 5 mm diameter) were prepared and polymerized for 20s with a light emitted diode unit. After fabrication, each sample was immediately immersed in 75 wt% ethanol/water solution used as extraction fluid and stored in the amber colored bottles at room temperature. Ethanol/water samples were taken (0.5 mL) at predefined time intervals:10 m (T1), 1 h (T2), 24h (T3) and 30 days (T4). These samples were analyzed by HPLC. The obtained data were analyzed with one-way ANOVA and Tukey HSD at significance level of p < 0.05. Results. Amount of eluted Bis-EMA and Bis-GMA from Tetric Evo Ceram Bulk Fill and amount of eluted TEGDMA and HEMA from X-tra Fill higher than others composites (p < 0.05). Significance. Residual monomers were eluted from bulk fill composite resins in all time periods and the amount of eluted monomers was increased with time. (C) 2015 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.
  • [ N/A ]
    Öğe
    Influence of eugenol on the push-out bond strengths of fiber posts cemented with different types of resin luting agents
    (Springer, 2013) Ozcan, Erhan; Cetin, Ali Riza; Capar, Ismail Davut; Tuncdemir, Ali Riza; Aydinbelge, Hale Ari
    This study evaluated the influence of eugenol on the push-out bond strengths of fiber posts cemented with different types of resin luting agents. Seventy-two extracted maxillary single-rooted canine teeth were randomly divided into two groups of 36 teeth. Group 1, the control group, was filled with gutta-percha only (i.e., did not receive eugenol), whereas group 2 was filled with a eugenol-containing sealer. All root canals were filled and each group was divided into three subgroups. The posts in each subgroup were cemented with the following materials: subgroup 1 with a 2-step self-etching adhesive system (Clearfil Liner Bond 2V + Panavia F); subgroup 2 with a 1-step self-etching adhesive (Panavia F); and subgroup 3 with a self-adhesive (Clearfil SA Cement). Dislodgement resistance was measured using a universal testing machine. All data were subjected to ANOVA using a factorial design and Tukey test (alpha = 0.05). The use of the eugenol-containing sealer significantly reduced the push-out bond strength of the fiber post (P < 0.05). The push-out bond strength of Panavia F was significantly higher than those of the other groups filled with the eugenol-containing sealer (P < 0.05). The Panavia F group was less susceptible to the inhibiting effect of eugenol than were the other evaluated groups when the fiber post was cemented in the canals filled with the eugenol-containing sealer.