    Effect of cement space on the marginal fit of CAD-CAM-fabricated monolithic zirconia crowns
    (Mosby-Elsevier, 2016) Kale, Ediz; Seker, Emre; Yilmaz, Burak; Ozcelik, Tuncer Burak
    Statement of problem. Monolithic zirconia crowns fabricated with computer-aided design and computer-aided manufacturing (CAD-CAM) have recently become a common practice for the restoration of posterior teeth. The marginal fit of monolithic zirconia crowns may be affected by different cement space parameters set in the CAD software. Information is scarce regarding the effect of cement space on the marginal fit of monolithic zirconia crowns fabricated with CAD CAM technology. Purpose. The purpose of this in vitro study was to evaluate the effect of cement space on the marginal fit of CAD-CAM-fabricated monolithic zirconia crowns before cementation. Material and methods. Fifteen right maxillary first molar typodont teeth with standardized anatomic preparations for complete-coverage ceramic crowns were scanned with a 3-dimensional laboratory scanner. Crowns were designed 3-dimensionally using software and then milled from presintered monolithic zirconia blocks in a computer numerical control dental milling machine. The cement space was set at 25 mu m around the margins for all groups, and additional cement space starting 1 mm above the finish lines of the teeth was set at 30 mu m for group 25-30, 40 mu m for group 25-40, and 50 mu m for group 25-50 in the CAD software. A total of 120 images (3 groups, 5 crowns per group, 8 sites per crown) were measured for vertical marginal discrepancy under a stereoscopic zoom microscope and the data were statistically analyzed with 1-way analysis of variance, followed by the Tukey honestly significant difference test (alpha=.05). Results. The results showed that different cement space values had statistically significant effect on the mean vertical marginal discrepancy value of tested crowns (P<.001). The mean marginal discrepancy was 85 mu m for group 25-30, 68 mu m for group 25-40, and 53 mu m for group 25-50. Conclusions. Within the limitations of this in vitro study, it was concluded that the cement space had a significant effect on the marginal fit of CAD-CAM-fabricated monolithic zirconia crowns. The marginal fit improved as the cement space decreased.
  • Küçük Resim
    Öğe
    Effect of fabrication stages and cementation on the marginal fit of CAD-CAM monolithic zirconia crowns
    (Mosby-Elsevier, 2017) Kale, Ediz; Yilmaz, Burak; Seker, Emre; Ozcelik, Tuncer Burak
    Statement of problem. Monolithic zirconia crowns fabricated using computer-aided design and computer-aided manufacturing (CAD-CAM) technology have recently become an alternative dental prosthetic treatment. The marginal fit of monolithic zirconia crown may be affected by different stages of the fabrication procedures in the laboratory and cementation. Information regarding the accuracy of fit of monolithic zirconia crowns at different stages of fabrication and cementation is limited. Purpose. The purpose of this in vitro study was to evaluate the effect of different stages of fabrication and cementation on the vertical marginal discrepancy (VMD) of CAD-CAM fabricated monolithic zirconia crowns. Material and methods. Six ivorine right maxillary first molar typodont teeth with standardized anatomic preparations for complete coverage ceramic crowns were scanned with a 3-dimensional laboratory scanner. Crowns were designed using CAD software and milled from presintered monolithic zirconia blocks in a 5-axis dental milling machine. A cement space of 25 pm for the margins and a 50-gm space starting 1 mm above the finish lines of the teeth were virtually set in the CAD software. A total of 144 measurements were performed on 6 specimens with 8 measurement locations in 3 different stages using stereoscopic zoom microscopy; after initial production of the crowns (post-sintering group), after glazing (post-glazing group), and after cementation (post-cementation group). The VMD values were statistically analyzed with 1-way repeated measures ANOVA and the Holm-Sidak method (alpha=.05). Results. Different stages of fabrication and cementation significantly affected the VMD of tested crowns (P=.003). The mean VMD was 38 gm for post-sintering group, 38 pm for post-glazing group, and 60 mu m for post-cementation group, with statistical differences between the post-sintering group, the post-cementation group (P<.002), and the post-glazing group and post-cementation group (P<.003); there were no statistical differences between the post-sintering group and the post-glazing group (P=.966). Conclusions. Within the limitations of this in vitro study, glazing did not significantly change the VMD of CAD-CAM monolithic zirconia crowns. Cementation significantly increased the VMD values.