Yazar "Turgut, Selvin" seçeneğine göre listele
Listeleniyor 1 - 6 / 6
Sayfa Başına Sonuç
Sıralama seçenekleri
Öğe Accelerated formation of BaTiO3 ceramics with mechanochemical processing in different liquids(Elsevier Science Sa, 2017) Akbas, Hatice Zehra; Aydin, Zeki; Guder, Ferhat; Turgut, SelvinBaTiO3 powders were synthesized from BaCO3 and TiO2 with mechanochemical processing using a shaker by solid-state reactions in distilled water, methanol, and acetone. Decomposition of BaCO3, disproportionation of the liquids and hydrous titanium oxide are led to formation of the BaTiO3 ceramics. The liquids are accelerated the formation of BaTiO3 dependent on the O-H bands of the liquids structure. More O-H bands increased the density of the calcined powders, and improved the microstructure of sintered BaTiO3 ceramics. The density of the calcined powders is 4.67, 3.66, and 3.49 g/cm(3) for the water, methanol, and acetone respectively. X-ray Diffraction (XRD) and Raman spectroscopy analysis were verified the structure of BaTiO3. The differences of the microstructure are clearly shown that the micrographs of sintered pellets by Scanning Electron Microscopy (SEM). Depending on the liquid, the process led directly to normal and abnormal grain growth of the sintered samples. (C) 2016 Elsevier B.V. All rights reserved.Öğe Effects of ultrasonication and conventional mechanical homogenization processes on the structures and dielectric properties of BaTiO3 ceramics(Elsevier Science Bv, 2017) Akbas, Hatice Zehra; Aydin, Zeki; Yilmaz, Onur; Turgut, SelvinThe effects of the homogenization process on the structures and dielectric properties of pure and Nb-doped BaTiO3 ceramics have been investigated using an ultrasonic homogenization and conventional mechanical methods. The reagents were homogenized using an ultrasonic processor with high-intensity ultrasonic waves and using a compact mixer-shaker. The components and crystal types of the powders were determined by Fourier-transform infrared spectroscopy (FTIR) and X-ray diffraction (XRD) analyses. The complex permittivity (epsilon', epsilon'') and AC conductivity (sigma') of the samples were analyzed in a wide frequency range of 20 Hz to 2 MHz at room temperature. The structures and dielectric properties of pure and Nb-doped BaTiO3 ceramics strongly depend on the homogenization process in a solid-state reaction method. Using an ultrasonic processor with high-intensity ultrasonic waves based on acoustic cavitation phenomena can make a significant improvement in producing high-purity BaTiO3 ceramics without carbonate impurities with a small dielectric loss. (C) 2016 Elsevier B.V. All rights reserved.Öğe Ferroelektrik malzemelerde kullanılan yeni tip seramiklerin üretimi ve karakterizasyonu(Hatay Mustafa Kemal Üniversitesi, 2018) Turgut, Selvin; Aydın, Zeki1900'lü yılların başlarından itibaren sentezlenip kullanılmaya başlanan katkılı ve katkısız BaTiO3, SrTiO3, (Ba/Sr)TiO3 seramikler sahip oldukları mekanik, elektrik, termal ve biyokimyasal özellikleri nedeniyle otomotiv, elektrik/elektronik, medikal teknolojiler, makine mühendisliği vb. endüstrilerde kendilerine uygulama alanı bulmaktadırlar. Bu tez kapsamında katkılı/katkısız BaTiO3, SrTiO3, (Ba/Sr)TiO3 seramik tozları henüz yeni kullanılmaya başlanan ultrasonik karıştırma tekniği kullanılarak katı hal sentez yöntemi ile sentezlenmiştir. Ultrasonik karıştırma tekniği ve çalkalama tekniği ile katkısız BaTiO3 seramiği sentezlenmiş; bu iki teknik arasındaki avantajlar ve dezavantajlar belirlenmiştir. Daha küçük tanecikli ve homojen kristal yapılar elde edilmesi, homojenizasyon süresinin kısalığı, XRD analizinde sinyal/gürültü oranının yüksek olması gibi avantajlı özelliklerinden dolayı ultrasonik karıştırma tekniği katkılı ve katkısız BaTiO3, SrTiO3, (Ba/Sr)TiO3 tozları üretimi için tercih edilmiştir. Katkı olarak farklı mol oranlarında Mn, K, In, Rb, Pr iyonları ilave edilerek formülasyonları yapılmıştır. Ba, Sr ve Ti yerine katkılanan iyonların katkılama miktarları farklı olmakla birlikte (mol cinsinden) % 0,05 - 60 arasında yapılmıştır. Katkılı ve katkısız seramik tozların morfolojik özellikleri, kristal yapısı ve tanecik boyutları X-ışını difraksiyonu (XRD), taramalı elektron mikroskobu (SEM) ve alan emisyon taramalı elektron mikroskobu (FESEM) cihazları kullanılarak incelenmiş, katkılamayla birlikte yapıda meydana gelen değişiklikler tartışılmıştır. Oluşturulan yapıların kimyasal analizi için, örnekler derişik hidroklorik asit ile çözülerek ya gravimetrik tayin metodu ya da atomik absorpsiyon spektrometresi ile analiz edilmiştir.Öğe Mechanical Properties and Corrosion Resistance of Borosintered Distaloy Steels(Springer, 2020) Turgut, Selvin; Gunen, AliDistaloy SA is a sponge iron powder (nominal composition: Fe-1.75Ni-1.5Cu-0.5Mo) widely used in the production of powder metallurgy (P/M) parts in the automotive industry. In this study, Distaloy SA powders were sintered in two different atmospheres, one consisting of pure Ar gas (traditional sintering) and the other consisting of a mixture of 90 wt.% B4C and 10 wt.% NaBF(4)powders (borosintering). To investigate the effects of the different sintering atmospheres, the P/M samples were characterized using density measurements, surface roughness tests, scanning electron microscopy, energy dispersive x-ray spectroscopy, x-ray diffraction, microhardness measurements, nanoindentation experiments, wear tests and corrosion tests. On the surface of the borosintered samples, a 160-325 mu m thick double-phase FeB + Fe2B boride layer was formed. The hardness (1405-1688 HV) and elastic modulus (122.21-162.42 GPa) of the surface were significantly improved with the borosintering treatment compared to conventional sintering (215-250 HV, 63.28-94.86 GPa). Borosintering also provided low friction coefficient values and an increased wear resistance compared to conventional sintering. A significant increase in corrosion resistance was also observed with the borosintering treatment in three different solutions. The corrosion rates of both sintered and borosintered samples were ranked as NaCl < HCl < H2SO4. The borosintered samples displayed superior corrosion resistance compared to the sintered samples, especially in the acid solutions. The results of this study show that significant cost savings can be achieved by combining the boriding and sintering treatments in a single borosintering process.Öğe Structural Differences of BaTiO3 Ceramics Modified by Ultrasonic and Mechanochemical Methods(Springer, 2018) Aydin, Zeki; Turgut, Selvin; Akbas, Hatice ZehraBarium titanate powders were synthesized by the modified solid-state method with ultrasonic (5 min) and mechanochemical (12 h) deagglomeration methods. The structure of the samples was verified using Fourier transform infrared spectroscopy (FT-IR) and X-ray diffractometer (XRD). Scanning electron microscopy (SEM) analysis of the powders showed that using ultrasonic deagglomeration significantly decreased the particle size with perfect homogeneity in the shortest time. The particle size of the powders was calculated as 44.7 nm and 80.4 nm for ultrasonic and mechanochemical deagglomeration, respectively. The sintered pellet by ultrasonic method had no abnormal grain growth, and the grain sizes were between 10 and 30 m. The pellet by mechanochemical method had an abnormal grain growth, and the grain sizes were between 10 and 100 m. The results showed that ultrasonication remarkably improved the structure of the samples in the shortest time.Öğe Ultrasonikasyon işleminde prob çapının TiO2 ve ZrO2 tozlarının yapı ve morfolojik özellikleri üzerine etkisi(2016) Akbaş, Hatice Zehra; Aydın, Zeki; Karahan, İsmail Hakkı; Dilsizoğlu, Tuncay; Turgut, SelvinBu çalışmada, ultrasonikasyon işleminde prob çapının, TiO2 ve ZrO2 tozlarının yapısı ve morfolojik özellikleri üzerine etkisi incelenmiştir. Tozlara7 mm ve 40 mm çaplarındaki titanyum prob ile üretilen yüksek yoğunluklu ultrases dalgalarına maruz bırakılmıştır. X-ışını Kırınım (XRD) analizi ile ultrasonikasyon işlemi uygulanan tozlarda bazı yüzeylerin ortadan kaybolduğu ve bazı yeni yüzeylerin ortaya çıktığı bulunmuştur. Taramalı Elektron Mikroskopi (SEM) analizi bu yöntemle mikronaltı tane boyutlu tozların elde edilebildiğini göstermiştir.Büyük genlikli ultrasesüreten 7 mm çaplı probun küçük genlikli ultrases üreten 40 mm çaplı probdan daha etkili olduğu görülmüştür