Experimental failure analysis of mechanically fastened joints with clearance in composite laminates under preload
Yükleniyor...
Dosyalar
Tarih
2008
Yazarlar
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Elsevier Sci Ltd
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
A failure investigation was performed to determine the failure mode and bearing strength of mechanically fastened bolted-joints in glass fiber reinforced epoxy laminated composite plates, experimentally. Two different geometrical parameters those are the edge distance-to-hole diameter ratio (E/D) and plate width-to-hole diameter ratio (W/D) were considered. For this purpose, E/D ratio was selected from 1 to 5, whereas W/D ratio was chosen from 2 to 5. Due to determining material parameters effect, laminated plates were stacked as three different group which are [0 degrees/0 degrees/45 degrees/-45 degrees](s), [0 degrees/0 degrees/45 degrees/45 degrees](s) and [0 degrees/0 degrees/30 degrees/30 degrees](s), symmetrically. In addition, the preload moments were applied as 0, 3 and 6 nm, since an important target of this study is to observe the changing of failure mechanism under various preloads. The experiments were also performed under a clearance, for this reason the diameters of the bolt and the circular bolt hole were fixed 5 and 6 mm, respectively. Results showed that failure modes and bearing strengths were considerable affected by the increasing of preloads. Furthermore, when the material and geometrical parameters of composite bolted-joints were changed, the failure behavior and the values of bearing strengths were fully influenced from this changing. (C) 2007 Elsevier Ltd. All rights reserved.
Açıklama
Anahtar Kelimeler
composite laminates, failure analysis, mechanically fastened joints, bearing strength, bearing mode
Kaynak
Materials & Design
WoS Q Değeri
Q3
Scopus Q Değeri
Q1
Cilt
29
Sayı
6