Effect of stacking sequences on failure behavior of pinned E-Glass/epoxy composite plates

Basit Öğe Kaydı
dc.contributor.authorŞen, Faruk
dc.contributor.authorPakdil, Murat
dc.date.accessioned2019-07-16T15:48:51Z
dc.date.available2019-07-16T15:48:51Z
dc.date.issued2008
dc.departmentHatay Mustafa Kemal Üniversitesien_US
dc.description.abstractIn this study, the effect of stacking sequences on failure behavior of pinned composite plates was investigated. The laminated composite plates were made from epoxy matrix and glass fibers as reinforcement material. To observe the influences of joint geometry and stacking sequence on the failure mechanism, failure analysis were carried out experimentally. The nine different laminated composite plates were tested. The edge distance-to-hole diameter ratio (E/D) of specimens was designed from 1 to 6. Besides, the specimen width-to-hole diameter ratio (W/D) was only considered as 6. Experimental results point out that failure behavior is strictly influenced from both stacking sequences and geometrical parameters of composite specimens.en_US
dc.description.abstractBu çalışmada, pim bağlantısı yapılmış kompozitlerin tabaka dizilişlerinin hasar davranışına etkisi incelenmiştir. Tabakalı kompozit plakalar epoksi matris ve takviye elemanı olarak cam liflerinden üretilmiştir. Bağlantı geometrisinin ve tabaka dizilişinin hasar oluşumu üzerine etkilerini gözlemlemek için hasar analizi deneysel olarak yapılmıştır. Dokuz farklı tabakalı kompozit plaka test edilmiştir. Deney numunelerinin serbest ucunun delik çapına oranı (E/D), 1’den 6’ya kadar farklı boyutlarda tasarlanmıştır. Bunun yanı sıra, numune genişliğinin delik çapına oranı (W/D), tüm numunelerde 6 olarak hazırlanmıştır. Deney sonuçları, kompozit numunelerin hazırlanmasındaki boyut değişkenleri ve tabaka dizilişlerinin hasar davranışını önemli bir biçimde etkilediğini göstermiştir.en_US
dc.identifier.endpage151en_US
dc.identifier.issn1302-0900
dc.identifier.issue2en_US
dc.identifier.startpage147en_US
dc.identifier.urihttps://trdizin.gov.tr/publication/paper/detail/T0RNeE5EQXc=
dc.identifier.urihttps://hdl.handle.net/20.500.12483/1167
dc.identifier.volume11en_US
dc.identifier.wosWOS:000447785200010en_US
dc.identifier.wosqualityN/Aen_US
dc.indekslendigikaynakWeb of Scienceen_US
dc.indekslendigikaynakTR-Dizinen_US
dc.language.isotren_US
dc.relation.ispartofPoliteknik Dergisien_US
dc.relation.publicationcategoryMakale - Ulusal Hakemli Dergi - Kurum Öğretim Elemanıen_US]
dc.rightsinfo:eu-repo/semantics/openAccessen_US
dc.subjectMühendisliken_US
dc.subjectOrtak Disiplinleren_US
dc.titleEffect of stacking sequences on failure behavior of pinned E-Glass/epoxy composite platesen_US
dc.title.alternativePim bağlantılı e-glass/epoxsi kompozit plakalarda tabaka dizilişlerinin hasar davranışına etkisien_US
dc.typeArticleen_US

Dosyalar

Orijinal paket
Listeleniyor 1 - 1 / 1
Küçük Resim
İsim:
Sen, Faruk 2008.pdf
Boyut:
201.84 KB
Biçim:
Adobe Portable Document Format
Açıklama:
Tam Metin / Full Text
İndir

Koleksiyon

TR-Dizin İndeksli Yayınlar Koleksiyonu
WoS İndeksli Yayınlar Koleksiyonu