Çocuk diş hekimliğinde farklı polisaj prosedürleri ile kullanılan restoratif materyallerin yüzey pürüzlülüğü ve renk değişimlerinin değerlendirilmesi

Basit Öğe Kaydı
dc.contributor.advisorBolgül, Behi̇ye
dc.contributor.authorPeker, Öykü
dc.date.accessioned2024-05-27T17:28:56Z
dc.date.available2024-05-27T17:28:56Z
dc.date.issued2022en_US
dc.departmentFakülteler, Diş Hekimliği Fakültesi, Çocuk Diş Hekimliği Ana Bilim Dalıen_US
dc.description.abstractGiriş ve Amaç: Çalışmamızda çocuk diş hekimliği kliniklerinde kullanılan 4 farklı restoratif materyalin (Equia Forte, G-aenial Universal Injectable, Fill-up, Estelite Universal Flow Super Low) 4 farklı polisaj prosedürü (Sof-Lex, OptiDisc, Identoflex Composite Polisher, Super-Snap) uygulaması sonucu yüzey pürüzlülüğü ve renk stabilitesi özelliklerinin değerlendirilmesi amaçlanmıştır. Gereç ve Yöntem: Her bir restoratif materyalden 32 adet olacak şekilde toplamda 128 adet örnek 4 farklı polisaj prosedürü ile cilalanmak üzere üretici firmaların talimatları doğrultusunda her bir materyal 6 mm çapında, 2 mm yüksekliğinde polietilen kalıplar içerisine yerleştirilerek hazırlanmıştır. (n=8) Bitim ve cila işlemlerinin ardından örnekler 24 saat 37°C distile suda bekletilmiştir. Ardından örneklerin yüzey pürüzlülüğü ve renk stabilitesi ölçümleri yapılmıştır. Yüzey pürüzlülüğü testi ölçümleri için Mustafa Kemal Üniversitesi Teknoloji ve Ar-Ge Uygulama ve Araştırma Merkezinde bulunan Hysitron TI 950 TriboIndenter cihazı kullanılmıştır. Renk stabilitesini belirlemek için bir spektrofotometre cihazı (VITA Easyshade® Advance 4.0 (VITA Zahnfabrik, Bad Sackingen, Germany) kullanılmıştır. Daha sonra örnekler kola çözeltisi içerisinde 1 hafta boyunca bekletilmiş ve sonrasında final renk ölçümleri yapılmıştır. Renk farkları CIEDE 2000 sistemine göre kaydedilmiştir. Bulgular: En düşük yüzey pürüzlülük değerleri G-aenial materyalinde, en yüksek yüzey pürüzlülük değerleri ise Equia materyalinde görülmüştür.(p<0,001) En düşük pürüzlülük değerleri Sof-Lex materyali ile en yüksek pürüzlülük değerleri ise İdentoflex materyali ile görülmüştür.(p=0,02) Tüm materyaller incelendiğinde en düşük pürüzlülük değerleri Super-Snap materyali ile cilananan G-aenial restoratif materyalinde, en yüksek pürüzlülük değerleri ise İdentoflex materyali ile cilanan Equia materyalinde görülmüştür. En yüksek renk stabilitesi Fill-up materyalinde, en düşük renk stabilitesi Estelite materyalinde görülmüştür. En düşük renk değişim değerleri Sof-Lex materyali ile en yüksek renk değişim değerleri OptiDisc materyali ile görülmüştür. Tüm materyaller incelendiğinde en düşük renk değişim değerleri Super-Snap materyali ile cilalanan G-aenial materyalinde, en yüksek renk değişim değerleri ise İdentoflex materyali ile cilalanan Equia materyalinde görülmüştür. Yüzey pürüzlülüğü ile renk değişimi arasında istatistiksel olarak anlamlı bir ilişki olduğu tespit edilmiştir. Sonuç: Bu bilgiler ışığında G-aenial materyalinin yüzey pürüzlülüğü açısından, Fill-up materyalinin ise renk stabilitesi açısından en başarılı sonuçları gösterdiği belirlenmiştir. En düşük renk değişim ve yüzey pürüzlülük değerleri Super-Snap materyali ile cilalanan G-aenial materyalinde görülmüştür. Klinik olarak daha başarılı sonuçlar için kullanılan restoratif materyale göre en uygun cila prosedürünün seçilmesi gerektiği anlaşılmıştır.en_US
dc.description.abstractIntroduction and Aim: In our study, 4 different polishing procedures (Sof-Lex, OptiDisc, Identoflex Composite Polisher, Super-Snap) application of 4 different restorative materials (Equia Forte, G-aenial Universal Injectable, Fill-up, Estelite Universal Flow Super Low) used in pediatric dentistry clinics as a result, it was aimed to evaluate the surface roughness and color stability properties. Materials and Methods: A total of 128 samples, 32 from each restorative material, were prepared by placing each material in 6 mm diameter, 2 mm high polyethylene molds to be polished with 4 different polishing procedures in accordance with the manufacturer's instructions.( n=8) Samples after finishing and polishing processes. It was kept in distilled water at 37°C for 24 hours. Then, surface roughness and color stability measurements of the samples were made. Hysitron TI 950 TriboIndenter device in Mustafa Kemal University Technology and R&D Application and Research Center was used for surface roughness test measurements. A spectrophotometer device (VITA Easyshade® Advance 4.0 (VITA Zahnfabrik, Bad Sackingen, Germany) was used to determine the color stability. Then the samples were kept in the coke solution for 1 week and then the final color measurements were made. Color differences were recorded according to the CIEDE 2000 system. Results: The lowest surface roughness values were observed in the G-aenial material, and the highest surface roughness values were observed in the Equia material. (p<0.001) The lowest roughness values were observed with the Sof-Lex material and the highest roughness values were observed with the Identoflex material (p=0.02). ) When all materials were examined, the lowest roughness values were observed in G-aenial restorative material polished with Super-Snap material, and the highest roughness values were observed in Equia material polished with Identoflex material. The highest color stability was observed in the Fill-up material, and the lowest color stability was observed in the Estelite material. The lowest color change values were seen with Sof-Lex material and the highest color change values were seen with OptiDisc material. When all materials were examined, the lowest color change values were observed in G-aenial material polished with Super-Snap material, and the highest color change values were observed in Equia material polished with Identoflex material. It was determined that there is a statistically significant relationship between surface roughness and color change. Conclusion: In the light of this information, it was determined that the G-aenial material showed the most successful results in terms of surface roughness and the Fill-up material in terms of color stability. The lowest color change and surface roughness values are polished with Super-Snap material. It was seen in G-aenial material. It has been understood that the most appropriate polishing procedure should be selected according to the restorative material used for clinically more successful results.en_US
dc.identifier.endpage107en_US
dc.identifier.startpage1en_US
dc.identifier.urihttps://tez.yok.gov.tr/UlusalTezMerkezi/TezGoster?key=kScA8XnrRb0WogX-qPGFkhLyrGSaY5a_MCHLjdldgIXtNAoNnab_eYhGkjxP23_3
dc.identifier.urihttps://hdl.handle.net/20.500.12483/4018
dc.identifier.yoktezid730874en_US
dc.language.isoturen_US
dc.publisherHatay Mustafa Kemal Üniversitesien_US
dc.relation.publicationcategoryTezen_US
dc.rightsinfo:eu-repo/semantics/openAccessen_US
dc.subjectDiş Hekimliğien_US
dc.subjectDentistryen_US
dc.subjectÇocuk diş hekimliğien_US
dc.subjectpolisaj prosedürlerien_US
dc.subjectrenk değişimien_US
dc.subjectyüzey pürüzlülüğü.en_US
dc.subjectPediatric dentistryen_US
dc.subjectpolishing proceduresen_US
dc.subjectcolor changeen_US
dc.subjectsurface roughness.en_US
dc.titleÇocuk diş hekimliğinde farklı polisaj prosedürleri ile kullanılan restoratif materyallerin yüzey pürüzlülüğü ve renk değişimlerinin değerlendirilmesien_US
dc.title.alternativeEvaluation of surface roughness and color changes of restorative materials used with different polishing procedures in pediatric dentistryen_US
dc.typeSpecialist Thesisen_US

Dosyalar

Orijinal paket
Listeleniyor 1 - 1 / 1
Küçük Resim
İsim:
730874.pdf
Boyut:
3.82 MB
Biçim:
Adobe Portable Document Format
Açıklama:
Tam Metin / Full Text
İndir

Koleksiyon

Tıpta Uzmanlık - Tez Koleksiyonu